Carbon structural steel plate is steel where the main alloying constituent is carbon, is a low carbon steel that exhibits good strength coupled with formability. It is easy to machine and fabricate and can besecurely welded. The steel can be galvanized to provide increased corrosion resistance.
| Name | carton steel plate/carton steel coil(Gi Coil) |
| Material | SPCC,SPCD,SPCE,ST12-15,DC01-06,Q195A-Q235A,Q195AF-Q235AF,Q295A(B)-Q345A(B) |
| Standard | API 5L, ASTM A53-2007, ASTM A671-2006, ASTM A252-1998, ASTM A450-1996, ASME B36.10M-2004, ASTM A523-1996, BS 1387, BS EN10296, BS6323, BS 6363, BS EN10219, GB/T 3091-2001, GB/T 13793-1992, GB/T9711 |
| Section Shape | Square, Rectangular, Round, |
| Surface Treatment | black/ galvanized/ coat /oiled /painting,etc |
| Thickness | Cold rolled/Hot rolled:0.1~300mm |
| Width | 1.5-3M can choose |
| Length | 3mm-2000m/2438/3048mm as customer' s requirement |
| Zinc coating weight | 40-600g/m2 |
| Size | 1000mm*2000mm, 1219mm*2438mm, 1219mm*3048mm, or as required |
| Color | Golden, Black , Sapphire Blue, Brown, Rose gold, Bronze, Purple, gray, silver, Champagne,violet, blue diamond, etc |
| Application | Building components, mechanical equipment |
| Lead time | 7 to 25 working days after the receipt of 30% deposit |
| Payment terms | 30%TT for deposit, 70% balance before shipment or LC at sight |
Chemical composition
| C | Cu | Fe | Mn | P | Si | S |
| 0.25～0.290 | 0.20 | 98.0 | 1.03 | 0.040 | 0.280 | 0.050 |
Mechanical behavior
| A36 | ultimate tensile strength | tensile strength, yield strength | Elongation at break (unit: 200mm) | Elongationat break(unit:50mm) | Elastic Modulus | Bulk modulus (typical value for steel) | Poisson's ratio | shear modulus |
| Metric | 400～550MPa | 250MPa | 20.0% | 23.0% | 200GPa | 140GPa | 0.260 | 79.3GPa |
| imperial | 58000～79800psi | 36300psi | 20.0% | 23.0% | 29000ksi | 20300ksi | 0.260 | 11500ksi |
Physical properties
| Physical properties | Metric | imperial |
| density | 7.85 g/cm3 | 0.284 lb/in3 |
Application scope
Bolted, riveted or welded structures for bridges, construction and oil rigs, etc.
Used for forming storage tanks, silos, bearing plates, clamps, rings, templates, clamps, sprockets, cams, gears, base plates, forgings, decorative works, piles, brackets, automotive and agricultural equipment, frames, machinery parts, etc.
Equivalent material
| 国标GB | 欧标EN | 美标ASTM | 德标DIN,WNr | 日标JIS | 法国标准AFNOR | 英国标准BS | 加拿大HG |
| Q235B | S235JR | A283C | St37-2 | SM400A | E24-2 | 40A/40B | 230G |
| 意大利UNI | 印度IS | 瑞士SS | 澳大利亚ONORM | 挪威NS | 西班牙UNE | 国际标准ISO | 葡萄牙NP |
| Fe360B | IS2062 | 1311/1312 | RSt360B | NS12123 | AE235B-FN | E235B/ Fe360B | FE360-B |